Muhammad Mahyiddin Ramli
Thumbnail Image
Preferred name
Muhammad Mahyiddin Ramli
Official Name
Muhammad Mahyiddin, Ramli
Alternative Name
Ramli, Muhammad Mahyiddin
Ramli, M. Muhammad
Ramli, M. M.
Ramli, M.
Ramli, Muhammad Mahyidin
Mahyiddin Ramli, Mohd
Ramli, Muhammad M.
Main Affiliation
Scopus Author ID
55891565000
Researcher ID
AAH-1285-2021

Research Output

Filters

2
Reset filters

Settings
Now showing 1 - 2 of 2
  • Publication
    Effect of Ni on the suppression of sn whisker formation in Sn-0.7Cu solder joint
    ( 2021)
    Aimi Noorliyana Hashim
    ;
    Mohd Arif Anuar Mohd Salleh
    ;
    Andrei Victor Sandu
    ;
    Muhammad Mahyiddin Ramli
    ;
    Khor Chu Yee
    ;
    Noor Zaimah Mohd Mokhtar
    ;
    Jitrin Chaiprapa
    The evolution of internal compressive stress from the intermetallic compound (IMC) Cu6Sn5 growth is commonly acknowledged as the key inducement initiating the nucleation and growth of tin (Sn) whisker. This study investigates the effect of Sn-0.7Cu-0.05Ni on the nucleation and growth of Sn whisker under continuous mechanical stress induced. The Sn-0.7Cu-0.05Ni solder joint has a noticeable effect of suppression by diminishing the susceptibility of nucleation and growth of Sn whisker. By using a synchrotron micro X-ray fluorescence (µ-XRF) spectroscopy, it was found that a small amount of Ni alters the microstructure of Cu6Sn5 to form a (Cu,Ni)6Sn5 intermetallic layer. The morphology structure of the (Cu,Ni)6Sn5 interfacial intermetallic layer and Sn whisker growth were investigated by scanning electron microscope (SEM) in secondary and backscattered electron imaging mode, which showed that there is a strong correlation between the formation of Sn whisker and the composition of solder alloy. The thickness of the (Cu,Ni)6Sn5 IMC interfacial layer was relatively thinner and more refined, with a continuous fine scallop-shaped IMC interfacial layer, and consequently enhanced a greater incubation period for the nucleation and growth of the Sn whisker. These verification outcomes proposes a scientifically foundation to mitigate Sn whisker growth in lead-free solder joint.
  • Publication
    Production of low temperature synthetic graphite
    ( 2023-04)
    Anis Syafiqa Rosman
    ;
    Ranjitha Navalan
    ;
    Muhammad Mahyiddin Ramli
    ;
    Norizah Abd Karim
    ;
    Mohd Fairus Ahmad
    ;
    Shazlina Johari
    ;
    Norshamsuri Ali @ Hasim
    ;
    Nurul Huda Osman
    Synthetic graphite is a material consisting of graphitic carbon which has been obtained by graphitizing a non-graphitic carbon. The growth in demand, particularly in customizing properties for certain usage has brought about research on viable alternative, low-cost, and environmentally pleasant synthetic graphite production. Biomass wastes are amongst appealing carbon precursors which have been broadly checked out as replacement carbon for graphite production. This research aimed to synthesize synthetic graphite from oil palm trunks at low temperatures (500 °C, 400 °C and 300 °C) under controlled conditions to determine the physical properties and properties of the graphite obtained. After the heat treatment process, the obtained samples were then characterized by using XRD, SEM and RAMAN characterizations. Based on SEM and RAMAN characterization, it can be seen that graphite that undergoes a 500 °C pyrolysis process shows the best results compare to graphite that undergoes a pyrolysis process at the temperatures of 300 °C and 400 °C. The graphite flakes and the peaks obtained for 500 °C graphite are obviously present. For XRD characterization, the best samples at 500 °C were chosen to be characterized. From the results, the sample shows slight behavior imitating the commercialized graphite. Hence, from the characterizations of the samples, it can be concluded that the best synthetic graphite produced was from the oil palm trunks heated at 500 ° C