Ag/TiO2 thin film was prepared by the sol-gel method through the hydrolysis of titanium tetraisopropoxide and silver nitrate solution. Spin coating method was used to get uniform film on ITO glass substrate followed by annealing process for 1 hour. After that, all the samples were characterised using GIXRD and FESEM and undergone water contact angle test and MB degradation. Silver ion concentrations were varied to observe the effect on crystalline state, morphology, wettability and photocatalytic properties. The results showed that Ag/TiO2 thin film was in anatase phase and it could degrade nearly 70% of methylene blue after 150 min illumination. The formed Ag/TiO2 thin film has excellent self-cleaning property with compact, continuous, smooth, and good hydrophilicity property.