Water based Remazol Orange was utilized as the dye sensitizer for dye sensitized solar cell. The annealing temperature of TiO2 working electrode was set at 450 °C. The performance of the device was investigated between dye concentrations of 0.25 mM and 2.5 mM at three different immersion times (3, 12 and 24 hours). The adsorption peak of the dye sensitizer was evaluated using UV-Vis-Nir and the device performance was tested using solar cell simulator. The results show that the performance was increased at higher dye concentration and longer immersion time. The best device performance was obtained at 0.2% for dye concentration of 2.5 mM immersed at 24 hours.