Insight on the structural aspect of ENR-50/TiO<inf>2</inf> hybrid in KOH/C<inf>3</inf>H<inf>8</inf>O medium revealed by NMR spectroscopy

The ring-opening reactions (ROR) of epoxide groups in epoxidized natural rubber/titania (ENR-50/TiO2) hybrid in potassium hydroxide/isopropanol medium were examined using NMR spectroscopy and supported by the FTIR technique. The thermal behaviour of the hybrid was also studied using TG/DTG and DSC analyses. The 1H NMR results suggested that 16.82% of ROR occurred in the hybrid, while the 13C NMR results exhibited five new peaks at δ 19.5, 71.0, 73.7, 91.7 and 94.4 ppm in the hybrid. 2D NMR, such as HMQC, HMBC and COSY techniques, further scrutinized these assignments. The FTIR spectrum exhibited Ti-O-C characteristics via the peak at 1028 cm−1. The TG/DTG results showed four steps of thermal degradation at 44–148, 219–309, 331–489 and 629–810 °C due to the existence of Ti moieties along with a polymer chain mixture (intact and ring-opened epoxide groups) of ENR-50, which in turn led to an increase in the Tg value of the hybrid to 27 °C compared to that of purified ENR-50 at −17.72 °C.