    Effect of polyethylene glycol and sodium dodecyl sulphate on microstructure and self-cleaning properties of graphene oxide/TiO2 thin film
    ( 2020-09-01)
    Azani A.
    ;
    Dewi Suriyani Che Halin
    ;
    Kamrosni Abdul Razak
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Norsuria Mahmed
    ;
    Muhammad Mahyiddin Ramli
    ;
    Mohd Arif Anuar Mohd Salleh
    ;
    Mohd Fairul Sharin Abdul Razak
    ;
    Ayu Wazira Azhari
    ;
    Chobpattana V.
    ;
    Kaczmarek L.
    In this study, a sol gel procedure for preparation of TiO2 thin films with graphene oxide (GO) was developed. The effect of PEG and SDS addition on the microstructure of the films as well as the photocatalytic activity of the thin film was also investigated. The morphology and surface structure of the films were studied by SEM and AFM while the photocatalytic activity of the films was analyzed by measuring the degradation of methylene blue under sunlight irradiation using UV-Vis spectrophotometer. It was found that GO/TiO2 thin film with PEG shows a smaller and porous particle while GO/TiO2 thin film with SDS formed a very smooth surface and very fine particles. Therefore, in AFM analysis reveals that surface roughness decreases with the addition of PEG and SDS. Finally, the photocatalytic activity showed that GO/TiO2 thin film with SDS have the most effective self-cleaning property which degrade 64% of methylene blue that act as model of contaminants.
      1
  • Publication
    Microstructural studies of ag/tio2 thin film; effect of annealing temperature
    ( 2022-01-01)
    Kamrosni A.R.
    ;
    Dewi Suriyani Che Halin
    ;
    Azliza A.
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Mohd Arif Anuar Mohd Salleh
    ;
    Norsuria Mahmed
    ;
    Chobpattana V.
    ;
    Kaczmarek L.
    ;
    Jez B.
    ;
    Nabialek M.
    Microstructures are an important link between materials processing and performance, and microstructure control is essential for any materials processing route where the microstructure plays a major role in determining the properties. In this work, silverdoped titanium dioxide (Ag/TiO2) thin film was prepared by the sol-gel method through the hydrolysis of titanium tetra-isopropoxide and silver nitrate solution. The sol was spin coated on ITO glass substrate to get uniform film followed by annealing process for 2 hours. The obtained films were annealed at different annealing temperatures in the range of 300°C-600°C in order to observe the effect on crystalline state, microstructures and optical properties of Ag/TiO2thin film. The thin films were characterized by X-Ray diffraction (XRD), scanning electron microscopy (SEM), and UV-Vis spectrophotometry. It is clearly seen, when the annealing temperature increases to 500°C, a peak at 2θ = 25.30° can be seen which refers to the structure of TiO2tetragonal anatase. The structure of Ag/TiO2thin film become denser, linked together, porous and uniformly distributed on the surface and displays the highest cut-off wavelength value which is 396 nm with the lowest band gap value, which is 3.10 eV.
      1
  • Publication
    Microstructural Study on Ag/TiO2 Thin Film
    ( 2022-07-01)
    Kamrosni Abdul Razak
    ;
    Dewi Suriyani Che Halin
    ;
    Azliza Azani
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Mohd Arif Anuar Mohd Salleh
    ;
    Norsuria Mahmed
    ;
    Chobpattana V.
    ;
    Kaczmarek L.
    ;
    Sandu A.V.
    ;
    Garus S.
    The synthesis of Ag/TiO2 thin film was carried out by the sol–gel spin coating method using ITO glass as a substrate in a short period of stirring time, which is less than 25 min. The produced films were annealed in a furnace at 500◦C for 1 h. Various concentrations of AgNO3, from 0.1 to 0.9 M, were added. The as-prepared films were characterized using X-ray diffraction, scanning electron microscopy, and atomic force microscopy. The results indicate that all films showed a single phase of anatase, TiO2. Ag/TiO2 thin films with 0.1 M of AgNO3 solution show that the elements form networks connecting Ag/TiO2 microstructures forming a porous, consistent, and continuous layer on the substrate surface.