Performance of fly ash based geopolymer incorporating palm kernel shell for lightweight concrete

A concrete which cement is totally replaced by source material such as fly ash and activated by highly alkaline solutions is known as geopolymer concrete. Fly ash is the most common source material for geopolymer because it is a by-product material, so it can get easily from all around the world. An investigation has been carried out to select the most suitable ingredients of geopolymer concrete so that the geopolymer concrete can achieve the desire compressive strength. The samples were prepared to determine the suitable percentage of palm kernel shell used in geopolymer concrete and cured for 7 days in oven. After that, other samples were prepared by using the suitable percentage of palm kernel shell and cured for 3, 14, 21 and 28 days in oven. The control sample consisting of ordinary Portland cement and palm kernel shell and cured for 28 days were prepared too. The NaOH concentration of 12M, ratio Na2SiO3 to NaOH of 2.5, ratio fly ash to alkaline activator solution of 2.0 and ratio water to geopolymer of 0.35 were fixed throughout the research. The density obtained for the samples were 1.78 kg/m3, water absorption of 20.41% and the compressive strength of 14.20 MPa. The compressive strength of geopolymer concrete is still acceptable as lightweight concrete although the compressive strength is lower than OPC concrete. Therefore, the proposed method by using fly ash mixed with 10% of palm kernel shell can be used to design geopolymer concrete.