Effect of anisotropic pores on the material properties of metakaolin geopolymer composites incorporated with corrugated fiberboard and rubber

This paper compares the compressive strength and thermal conductivity of metakaolin geopolymer (MKG) incorporated with anisotropic and isotropic pores. MKG was prepared by activation with sodium hydroxide and sodium silicate. Corrugated fiberboard and rubber were included to create anisotropy of pores, and they were added in 3, 5, and 7 layers. Hydrogen peroxide and surfactant were added to generate isotropic pores. For geopolymer with corrugated fiberboard (MKG-C) and rubber (MKG-R), compressive test and thermal conductivity measurement were performed in perpendicular and parallel direction to the flat surface of fiberboard and rubber. The result showed that MKG-C and MKG-R exhibited mechanical and insulation anisotropically. The highest compressive strength was achieved in the parallel loading direction while the lowest thermal conductivity was attained in the perpendicular direction. MKG-C possessed better compressive strength of 26.9 MPa loaded in the parallel direction. The compressive strength performance of MKG-C was greater than MKG-R because of the fibrous-like structure, which further contributes to the strength. The thermal conductivity was low (0.15–0.20 W/mK) for both MKG-C and MKG-R. The anisotropy of pores led to high strength retention and improvement of thermal insulating properties. These properties were contrary to geopolymer with isotropic pores (MKG-F), which have excellent thermal insulating properties but low compressive strength to be eligible for structural applications.