In this research, we prepared pure kenaf composites and kenaf/glass fibre hybrid composites using the hand lay-up procedure. Also, we studied the weather effects on the mechanical, morphological and thermal properties of the pure kenaf and the kenaf/glass fibre hybrid composites. Before the weathering conditions, we determined that the tensile strength of the kenaf /glass fibre hybrid composite was 70.9 MPa, while the tensile modulus was 3030 MPa. However, during the first weathering month, there was a decrease in the tensile modulus values, which further decreased as the weathering continued. Also, there was a significant difference in the tensile modulus reduced values between the pure kenaf and the glass fibre-reinforced kenaf composites, which indicated that the glass fibre was a good reinforcement option, and could be successfully used for producing high performing composites. Based on the flexural strength results obtained, it could be noted that the natural fibre composites could not withstand the environmental conditions, as they displayed poor wettability, a higher moisture adsorption and were incompatible with some of the polymeric matrices. As they had higher moisture absorption properties, they formed voids within the composites that could decrease the composite mechanical properties like the flexural strength or the flexural modulus, which was supported BY our SEM results. However, some of the modifications do tend to improve the mechanical properties, which help in improving the composite performance with a proper composite formulation during modification. Our results showed that the thermal properties of the kenaf and the kenaf hybrid composites are significantly affected by the weather, wherein the composites display a slow and gradual initial weight loss till a massive weight loss was observed at temperatures around 390°C. However, as the weathering increased, the weight loss was seen to occur at even low temperatures of 290°C. This phenomenon was because of the moisture absorption, which was seen to increase it, and the moisture weakened the molecular interfacial bonds.