Co-pyrolysis of rubberwood sawdust (RWS) waste and polypropylene (PP) was carried out at different temperatures (450,500,550, and 600°C) with biomass to plastics ratio 1:1 by using fixed bed drop-type pyrolyzer. The yield of pyrolysis oil has an increasing trend as the temperature increased from 450°C to 550°C. However, the pyrolysis oil yield dropped at a temperature of 600°C. Co-pyrolysis of RWS and PP generated maximum pyrolysis oil with 36.47 wt.% at 550°C. The result is compared with the pyrolysis of RWS only without plastics, with the same feedstock, and the maximum pyrolysis oil yield obtained was 33.3 wt.%. The water content in pyrolysis oil of co-pyrolysis RWS with PP is lower than RWS only with 54.2 wt.% and 62 wt.% respectively. Hydrocarbons, acyclic olefin, alkyl, and aromatic groups are the major compound in the pyrolysis oil from the co-pyrolysis process. Carbon monoxide (52.2 vol.%) and carbon dioxide (38.2 vol.%) are the major gas components.