In this study, the mechanical properties and maximum failure load of a bulk and T-joints subjected to tensile loading were investigated experimentally. A bulk and the T-joint specimens were fabricated and tested in order to investigate the effects of temperature conditions on the failure of the joints. The adherent and adhesive used for T-joint are 304 L stainless steel and Hysol E 214 HP with the adhesive thickness of 1.0 mm. The tensile test of the bulk specimen and adhesively T-joint were conducted by using a universal testing machine (UTM) at room temperature (RT), 55 °C, 75 °C, 100 °C and 120 °C, respectively. It was found that as the temperature increases, the failure force strength decreases for bulk and T-joint specimen. Data obtained from the tests at 120 °C showed the failure force of the bulk adhesive decreased by approximately 44 % compared to the specimen tested at RT. Next, the bulk of Hysol failure force result was compared with Araldite at RT and 100 °C. Araldite data was taken from the previous study [1]. It has also been found that the bulk for Hysol has higher failure force compared to Araldite at RT and 100 °C.