  • Publication
    Improvements of flexural properties and thermal performance in thin geopolymer based on fly ash and ladle furnace slag using borax decahydrates
    ( 2022)
    Ng Yong-Sing
    ;
    Liew Yun Ming
    ;
    Heah Cheng Yong
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Phakkhananan Pakawanit
    ;
    Petrica Vizureanu
    ;
    Mohd Suhaimi Khalid
    ;
    Ng Hui-Teng
    ;
    Hang Yong-Jie
    ;
    Marcin Nabiałek
    ;
    Paweł Pietrusiewicz
    ;
    Sebastian Garus
    ;
    Wojciech Sochacki
    ;
    Agata Śliwa
    This paper elucidates the influence of borax decahydrate addition on the flexural and thermal properties of 10 mm thin fly ash/ladle furnace slag (FAS) geopolymers. The borax decahydrate (2, 4, 6, and 8 wt.%) was incorporated to produce FAB geopolymers. Heat treatment was applied with temperature ranges of 300 °C, 600 °C, 900 °C, 1000 °C and 1100 °C. Unexposed FAB geopolymers experienced a drop in strength due to a looser matrix with higher porosity. However, borax decahydrate inclusion significantly enhanced the flexural performance of thin geopolymers after heating. FAB2 and FAB8 geopolymers reported higher flexural strength of 26.5 MPa and 47.8 MPa, respectively, at 1000 °C as compared to FAS geopolymers (24.1 MPa at 1100 °C). The molten B2O3 provided an adhesive medium to assemble the aluminosilicates, improving the interparticle connectivity which led to a drastic strength increment. Moreover, the borax addition reduced the glass transition temperature, forming more refractory crystalline phases at lower temperatures. This induced a significant strength increment in FAB geopolymers with a factor of 3.6 for FAB8 at 900 °C, and 4.0 factor for FAB2 at 1000 °C, respectively. Comparatively, FAS geopolymers only achieved 3.1 factor in strength increment at 1100 °C. This proved that borax decahydrate could be utilized in the high strength development of thin geopolymers.
      3  21
  • Publication
    Self-Fluxing mechanism in geopolymerization for Low-Sintering temperature of ceramic
    ( 2021)
    Noorina Hidayu Jamil
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Faizul Che Pa
    ;
    Hasmaliza Mohamad
    ;
    Wan Mohd Arif W Ibrahim
    ;
    Penphitcha Amonpattaratkit
    ;
    Joanna Gondro
    ;
    Wojciech Sochacki
    ;
    Norfadhilah Ibrahim
    Kaolin, theoretically known as having low reactivity during geopolymerization, was used as a source of aluminosilicate materials in this study. Due to this concern, it is challenging to directly produce kaolin geopolymers without pre-treatment. The addition of ground granulated blast furnace slag (GGBS) accelerated the geopolymerization process. Kaolin–GGBS geopolymer ceramic was prepared at a low sintering temperature due to the reaction of the chemical composition during the initial stage of geopolymerization. The objective of this work was to study the influence of the chemical composition towards sintering temperature of sintered kaolin–GGBS geopolymer. Kaolin–GGBS geopolymer was prepared with a ratio of solid to liquid 2:1 and cured at 60 °C for 14 days. The cured geopolymer was sintered at different temperatures: 800, 900, 1000, and 1100 °C. Sintering at 900 °C resulted in the highest compressive strength due to the formation of densified microstructure, while higher sintering temperature led to the formation of interconnected pores. The difference in the X-ray absorption near edge structure (XANES) spectra was related to the phases obtained from the X-ray diffraction analysis, such as akermanite and anothite. Thermal analysis indicated the stability of sintered kaolin–GGBS geopolymer when exposed to 1100 °C, proving that kaolin can be directly used without heat treatment in geopolymers. The geopolymerization process facilitates the stability of cured samples when directly sintered, as well as plays a significant role as a self-fluxing agent to reduce the sintering temperature when producing sintered kaolin–GGBS geopolymers.