  • Publication
    Cold-pressed fly ash geopolymers: effect of formulation on mechanical and morphological characteristics
    ( 2021)
    Ong Shee-Ween
    ;
    Heah Cheng Yong
    ;
    Lynette Wei Ling Chan
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Ho Li Ngee
    ;
    Liew Yun Ming
    ;
    Ooi Wan-En
    ;
    Ng Yong-Sing
    ;
    Nur Ain Jaya
    This research uses low alkali activator content and cold pressing technique for fly ash-based geopolymers formation under room temperature condition. The geopolymers were prepared using four different parameters: fly ash/alkali activator ratio, sodium hydroxide concentration, sodium silicate/sodium hydroxide ratio and pressing force. The results indicated that the compressive strength (114.2 MPa) and flexural strength (29.9 MPa) of geopolymers maximised at a fly ash/alkali activator ratio of 5.5, a 14 M sodium hydroxide concentration, a sodium silicate/sodium hydroxide ratio of 1.5 and a pressing force of 5 tons (pressing stress of 100.0 MPa and 155.7 MPa for compressive and flexural samples, respectively). The degree of reaction (40.1%) enhanced the structure compactness with minimum porosity. The improved mechanical properties confirmed that a high strength pressed geopolymer could be formed at low alkali activator content without the aid of temperature.
  • Publication
    Correlation between pore structure, compressive strength and thermal conductivity of porous metakaolin geopolymer
    ( 2020)
    Nur Ain Jaya
    ;
    Liew Yun Ming
    ;
    Heah Cheng Yong
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Kamarudin Hussin
    This paper investigates the effect of mixing parameters (that are, alkali concentration, AA ratio, and MK/ AA ratio) on the thermal conductivity of metakaolin geopolymers. The combination effect of foaming agent (H2O2) and surfactant (Tween 80) on the physical properties, compressive strength, and pore characteristic was also elucidated. Results showed that metakaolin geopolymer with maximum compressive strength of 33 MPa, bulk density of 1680 kg/m3 , porosity of 18% and thermal conductivity of 0.40 W/mK were achieved with alkali concentration of 10 M, AA ratio of 1.0 and MK/AA ratio of 0.8. Gradation analysis demonstrated that AA ratio was the strength determining factor. Whilst, thermal conductivity was dependent on the MK/AA ratio. Adding H2O2 and surfactant produced geopolymer foam with acceptable compressive strength (0.4–6 MPa). The geopolymer foam had bulk density of 471–1212 kg/m3 , porosity of 36–86% and thermal conductivity of 0.11–0.30 W/mK. Pore structure, size, and distribution were governed by H2O2 and surfactant dosages that have a great impact on the compressive strength. Narrower pore distribution and smaller pore diameter were achieved when both foaming agent and surfactant were used instead of foaming agent alone. The pore size and distribution varied to a greater extent with varying H2O2 contents. Surfactant illustrated distinct pore stabilizing effect at low H2O2 (<0.75 wt%) which diminished at high H2O2 content. In terms of thermal conductivity, even with increasing porosity at high H2O2 and surfactant content, the thermal conductivity did not show substantial reduction due to the interconnected pores as a result of pore coalescence