Formation of bio-based derived dicalcium silicate ceramics via mechanochemical treatment: physical, XRD, SEM and FTIR analyses

2023 , Siti Nur Hazwani Yunus , Khor Shing Fhan , Banjuraizah Johar , Nur Maizatul Shima Adzali , Nur Hazlinda Jakfar , Cheng Ee Meng , Emma Ziezie Mohd Tarmizi , Zainal Abidin Talib

Beta-dicalcium silicate plays an important role in modern technology, but its tendency for polymorphic transformation results in the dusting phenomenon, is a major challenge. Therefore, mechanochemical treatment is used to reduce the particle size to retain the stability of the polymorph. In this study, pure dicalcium silicate ceramics of β-monoclinic structure with P 121/c1 space group were synthesized using calcium oxide and silicate powders derived from calcined eggshells and rice husks, respectively. The powders were mixed in a 2:1 molar ratio by mechanochemical treatment and heat-treated in the air at temperatures ranging from 900°C to 1100°C for 2 h. The results reveal that pure beta-dicalcium silicate formed at 1100°C without adding stabilizers. The properties of the pristine and sintered bodies were characterized by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and scanning electron microscopy (SEM). SEM revealed that the grain and pore sizes increase with rising sintering temperatures. FTIR spectra indicate the existence of Si-O bonds in tetrahedrons on all the samples. The sample sintered at 1000°C attains the lowest bulk density (1.2463 g/cm3), whereas the apparent porosity is the highest (62.5%). The reason for this trend is due to the decomposition of carbonate into CO2 gas. The densification onset for the sample sintered at 1100°C as the bulk density rises and grain size achieves 6.06 μm. This study further explains the effect of sintering temperatures on the physical, structural, and morphological properties of Ca2SiO4 which would also be useful for further optimization of its use.-4 SiO4.

View
Thumbnail Image
Publication

Effect of sintering temperature on dielectric and electrical properties of bio-waste derived beta-dicalcium silicate

2023 , Siti Nur Hazwani Mohd Yunus , Khor Shing Fhan , Nur Hazlinda Jakfar , Banjuraizah Johar , Emma Ziezie Mohd Tarmizi , Cheng Ee Meng , Nur Maizatul Shima Adzali , Zainal Abidin Talib

Beta-dicalcium silicate ceramics were synthesized by mechanochemical-assisted solid-state reaction route using rice husks and chicken eggshells as silica and calcium oxide sources. The ceramics were sintered at 900, 1000, and 1100 °C for 2 h in air. The effect of sintering temperature on these ceramics' morphological, breakdown strength, dielectric, and electrical properties was investigated. It was found that the ceramic sintered at the optimized temperature of 1100 °C formed the pure β-dicalcium silicate (β-Ca2SiO4). Scanning electron micrographs showed that with the increase in sintering temperature, the average grain size and pore size of the sintered ceramics increased while the grain boundary density decreased, which promoted the breakdown path and resulted in a decrease in breakdown strength. The dielectric behavior examined from 25 to 300 °C and in a frequency range of 4–5 MHz found that the dielectric constant and loss tangent decreased with increasing frequency. Nyquist plot of impedance confirmed a non-Debye type relaxation, and grain and grain boundary contributions were revealed from equivalent circuit fitting. Variations of impedance spectroscopy reflect the positive and negative temperature coefficient of resistance behavior for these ceramics. Electric modulus spectra revealed that with the sintering temperature increase, the samples' conductivity activation energies increased from 0.35 to 0.46 eV. All the sintered samples attained low dielectric loss (0.004 < tanδ < 0.1) above 103 Hz, which makes them suitable materials for capacitor application.