The Mg-1wt.%Ca alloy was fabricated using powder metallurgy method. The anodizing process were done by using different voltage (5V, 15V, 25V) and concentration of KOH (0.1M, 0.5M, 1.0M). The surface changes on PM Mg/1wt.%Ca resulted by anodizing was analyzed using SEM-EDX and XRD pattern. Meanwhile, surface hardness was measured by micro-Vickers hardness machine. The experiment found different XRD pattern between all non-anodized and anodized samples. The study found that increasing the voltage will increase the hardness while increasing KOH concentration reduced the hardness. The relation of the hardness and oxide film formation can be analyzed using SEM-EDX and XRD pattern. The optimum value for voltage, KOH concentration and hardness are 25V, 0.1M and 27.2 HV. The XRD detect the changes in PM Mg/1wt.% Ca indicates the oxide film formation.