  • Publication
    Influence of filler surface modification on static and dynamic mechanical responses of rice husk reinforced linear low-density polyethylene composites
    ( 2022-01-01)
    Mohd Firdaus Omar
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Sam Sung Ting
    ;
    Jez B.
    ;
    Nabialek M.
    ;
    Akil H.M.
    ;
    Nik Noriman Zulkepli
    ;
    Shayfull Zamree Abd. Rahim
    ;
    Azmi A.
    Filler surface modification has become an essential approach to improve the compatibility problem between natural fillers and polymer matrices. However, there is limited work that concerns on this particular effect under dynamic loading conditions. Therefore, in this study, both untreated and treated low linear density polyethylene/rice husk composites were tested under static (0.001 s-1, 0.01 s-1and 0.1 s-1) and dynamic loading rates (650 s-1, 900 s-1and 1100 s-1) using universal testing machine and split Hopkinson pressure bar equipment, respectively. Rice husk filler was modified using silane coupling agents at four different concentrations (1, 3, 5 and 7% weight percentage of silane) at room temperature. This surface modification was experimentally proven by Fourier transform infrared and Field emission scanning electron microscopy. Results show that strength properties, stiffness properties and yield behaviour of treated composites were higher than untreated composites. Among the treated composites, the 5% silane weight percentage composite shows the optimum mechanical properties. Besides, the rate of sensitivity of both untreated and treated composites also shows great dependency on strain rate sensitivity with increasing strain rate. On the other hand, the thermal activation volume shows contrary trend. For fracture surface analysis, the results show that the treated LLDPE/RH composites experienced less permanent deformation as compared to untreated LLDPE/RH composites. Besides, at dynamic loading, the fracture surface analysis of the treated composites showed good attachment between RH and LLDPE.
      1
  • Publication
    Influence of filler surface modification on static and dynamic mechanical responses of rice husk reinforced linear low-density polyethylene composites
    ( 2021)
    Mohd Firdaus Omar
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Sam Sung Ting
    ;
    B. Jeż
    ;
    M. Nabiałek
    ;
    Hazizan Md Akil
    ;
    Nik Noriman Zulkepli
    ;
    Shayfull Zamree Abd. Rahim
    ;
    Azida Azmi
    Filler surface modification has become an essential approach to improve the compatibility problem between natural fillers and polymer matrices. However, there is limited work that concerns on this particular effect under dynamic loading conditions. Therefore, in this study, both untreated and treated low linear density polyethylene/rice husk composites were tested under static (0.001 s –1, 0.01 s –1 and 0.1 s –1) and dynamic loading rates (650 s –1, 900 s –1 and 1100 s –1) using universal testing machine and split Hopkinson pressure bar equipment, respectively. Rice husk filler was modified using silane coupling agents at four different concentrations (1, 3, 5 and 7% weight percentage of silane) at room temperature. This surface modification was experimentally proven by Fourier transform infrared and Field emission scanning electron microscopy. Results show that strength properties, stiffness properties and yield behaviour of treated composites were higher than untreated composites. Among the treated composites, the 5% silane weight percentage composite shows the optimum mechanical properties. Besides, the rate of sensitivity of both untreated and treated composites also shows great dependency on strain rate sensitivity with increasing strain rate. On the other hand, the thermal activation volume shows contrary trend. For fracture surface analysis, the results show that the treated LLDPE/RH composites experienced less permanent deformation as compared to untreated LLDPE/RH composites. Besides, at dynamic loading, the fracture surface analysis of the treated composites showed good attachment between RH and LLDPE.
      2  11
  • Publication
    Influence of filler surface modification on static and dynamic mechanical responses of rice husk reinforced linear low-density polyethylene composites
    ( 2021)
    Mohd Firdaus Omar
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Sam Sung Ting
    ;
    B. Jeż
    ;
    M. Nabiałek
    ;
    Hazizan Md Akil
    ;
    Nik Noriman Zulkepli
    ;
    Shayfull Zamree Abd. Rahim
    ;
    Azida Azmi
    Filler surface modification has become an essential approach to improve the compatibility problem between natural fillers and polymer matrices. However, there is limited work that concerns on this particular effect under dynamic loading conditions. Therefore, in this study, both untreated and treated low linear density polyethylene/rice husk composites were tested under static (0.001 s–1, 0.01 s–1 and 0.1 s–1) and dynamic loading rates (650 s–1, 900 s–1 and 1100 s–1) using universal testing machine and split Hopkinson pressure bar equipment, respectively. Rice husk filler was modified using silane coupling agents at four different concentrations (1, 3, 5 and 7% weight percentage of silane) at room temperature. This surface modification was experimentally proven by Fourier transform infrared and Field emission scanning electron microscopy. Results show that strength properties, stiffness properties and yield behaviour of treated composites were higher than untreated composites. Among the treated composites, the 5% silane weight percentage composite shows the optimum mechanical properties. Besides, the rate of sensitivity of both untreated and treated composites also shows great dependency on strain rate sensitivity with increasing strain rate. On the other hand, the thermal activation volume shows contrary trend. For fracture surface analysis, the results show that the treated LLDPE/RH composites experienced less permanent deformation as compared to untreated LLDPE/RH composites. Besides, at dynamic loading, the fracture surface analysis of the treated composites showed good attachment between RH and LLDPE.