Effect of polyethylene glycol and sodium dodecyl sulphate on microstructure and self-cleaning properties of graphene oxide/TiO2 thin film
The effect of GO/TiO2 thin film during photodegradation of methylene blue dye
1 - 2 of 2
Publication
In this study, a sol gel procedure for preparation of TiO2 thin films with graphene oxide (GO) was developed. The effect of PEG and SDS addition on the microstructure of the films as well as the photocatalytic activity of the thin film was also investigated. The morphology and surface structure of the films were studied by SEM and AFM while the photocatalytic activity of the films was analyzed by measuring the degradation of methylene blue under sunlight irradiation using UV-Vis spectrophotometer. It was found that GO/TiO2 thin film with PEG shows a smaller and porous particle while GO/TiO2 thin film with SDS formed a very smooth surface and very fine particles. Therefore, in AFM analysis reveals that surface roughness decreases with the addition of PEG and SDS. Finally, the photocatalytic activity showed that GO/TiO2 thin film with SDS have the most effective self-cleaning property which degrade 64% of methylene blue that act as model of contaminants.
Publication
Titanium (IV) isopropoxide (TTIP) was used to synthesize GO/TiO2 thin films using a sol-gel spin-coating method onto a glass substrate, undergoing an heat tretment at 350 °C. Several amounts of graphene oxide (GO) (0-20mg) were weighed into a sol solution of TiO2 to produce GO/TiO2 thin films. The thin film samples were characterized by X-ray diffraction (XRD) to analyze the samples’ phase and by scanning electron microscopy (SEM) to analyze the samples’ microstructure. Physical testing such as water contact angle (WCA) was analyzed using an optical microscope with J-Image software. In contrast, the optical band gap and photodegradation of methylene blue under sunlight irradiation of the thin film was analyzed using UV-VIS spectrophotometry. GO5 thin film sample showed low-intensity anatase phase formation, where the microstructure revealed a larger surface area with the addition of GO. WCA reveals that GO/TiO2 thin film exhibits super hydrophilic properties where the angle decreases from 37.83° to 4.11°. The optical result shows that GO has improved the absorption edges by expanding into visible regions. Moreover, due to the existence of GO 3.30 eV band gap energy of TiO2 decreases from to 3.18 eV obtained by GO5. The improved adsorption edge allows Ti3+, O2 and interstitial states to be formed in low valence states with energy underneath than in the TiO2 band gap. Therefore, the photodegradation of methylene blue (MB) dye increases from 48 % to 59 % in the GO/TiO2 thin film.