Mechanical performance, microstructure, and porosity evolution of fly ash geopolymer after ten years of curing age

2023 , Ikmal Hakem A. Aziz , Mohd. Mustafa Al Bakri Abdullah , Rafiza Abd Razak , Zarina Yahya , Mohd Arif Anuar Mohd Salleh , Jitrin Chaiprapa , Catleya Rojviriya , Petrica Vizureanu , Andrei Victor Sandu , Muhammad Faheem Mohd. Tahir , Alida Abdullah , Liyana Jamaludin

This paper elucidates the mechanical performance, microstructure, and porosity evolution of fly ash geopolymer after 10 years of curing age. Given their wide range of applications, understanding the microstructure of geopolymers is critical for their long-term use. The outcome of fly ash geopolymer on mechanical performance and microstructural characteristics was compared between 28 days of curing (FA28D) and after 10 years of curing age (FA10Y) at similar mixing designs. The results of this work reveal that the FA10Y has a beneficial effect on strength development and denser microstructure compared to FA28D. The total porosity of FA10Y was also lower than FA28D due to the anorthite formation resulting in the compacted matrix. After 10 years of curing age, the 3D pore distribution showed a considerable decrease in the range of 5–30 µm with the formation of isolated and intergranular holes.

View
No Thumbnail Available
Publication

The Suitability of Photocatalyst Precursor Materials in Geopolymer Coating Applications: A Review

2022-09-01 , Liyana Jamaludin , Rafiza Abd Razak , Mohd. Mustafa Al Bakri Abdullah , Vizureanu P. , Bras A. , Imjai T. , Sandu A.V. , Shayfull Zamree Abd. Rahim , Heah Cheng Yong

Today, the building and construction sector demands environmentally friendly and sustainable protective coatings using inorganic coating materials for safe, non-hazardous, and great performance. Many researchers have been working on sustainable solutions to protect concrete and metal infrastructures against corrosion and surface deterioration with the intention of introducing green alternatives to conventional coatings. This article presents a review of developments of geopolymer pastes doped with different types of photocatalyst precursors including factors affecting geopolymer properties for enhancing coating with photocatalytic performance. Photodegradation using geopolymer photocatalyst has great potential for resolving harmless substances and removing pollutants when energized with ultraviolet (UV) light. Although geopolymer is a potentially new material with great properties, there has been less research focusing on the development of this coating. This study demonstrated that geopolymer binders are ideal precursor support materials for the synthesis of photocatalytic materials, with a significant potential for optimizing their distinctive properties.

View
No Thumbnail Available
Publication

Geopolymer coating paste on concrete for photocatalytic performance

2021-05-03 , Liyana Jamaludin , Rafiza Abd Razak , Mohd. Mustafa Al Bakri Abdullah , Kusbiantoro A. , Zarina Yahya , Alida Abdullah , Sandu A.V.

Construction materials mainly used Portland cement as raw materials mainly caused global warming effect around the world. This article report a review on a research work carried out on the use of geopolymer coating on the concrete surface with catalyst for a good adsorption and efficiency via photocatalytic activity using sunlight. The geopolymer paste deposited by coating on the concrete or other building construction surface. The geopolymer paste were prepared by mixing aluminosilicates material with alkaline activator added with catalyst materials such as titanium dioxide and zinc oxide. The performance of geopolymer coating in removal of dyes reported comparable with other materials. Photocatalytic activity performance evaluate by adsorption of dyes onto geopolymer.

View
No Thumbnail Available
Publication

Fly Ash porous material using geopolymerization process for high temperature exposure

2012-04-10 , Mohd. Mustafa Al Bakri Abdullah , Liyana Jamaludin , Kamarudin Hussin , Mohamed Bnhussain , Che Mohd Ruzaidi Ghazali , Mohd Izzat Ahmad

This paper presents the results of a study on the effect of temperature on geopolymers manufactured using pozzolanic materials (fly ash). In this paper, we report on our investigation of the performance of porous geopolymers made with fly ash after exposure to temperatures from 600 °C up to 1000 °C. The research methodology consisted of pozzolanic materials (fly ash) synthesized with a mixture of sodium hydroxide and sodium silicate solution as an alkaline activator. Foaming agent solution was added to geopolymer paste. The geopolymer paste samples were cured at 60 °C for one day and the geopolymers samples were sintered from 600 °C to 1000 °C to evaluate strength loss due to thermal damage. We also studied their phase formation and microstructure. The heated geopolymers samples were tested by compressive strength after three days. The results showed that the porous geopolymers exhibited strength increases after temperature exposure.

View
No Thumbnail Available
Publication

Bahan geopolimer : Pemprosesan, Pencirian dan Aplikasi

2015 , Mohd. Mustafa Al Bakri Abdullah , Zarina Yahya , Alida Abdullah , Rafiza Abd Razak , Kamarudin Hussin , Liyana Jamaludin , Muhammad Faheem Mohd. Tahir

Buku Bahan Geopolimer: Pemprosesan, Pencirian dan Aplikasi adalah sebuah buku yang membincangkan beberapa aspek penting mengenai bahan geopolimer seperti pemprosesan, perincian, aplikasi dan sifat bahan geopolimer dalam teknologi konkrit. Buku ini juga menerangkan secara terperinci tentang bahan geopolimer dari aspek teori, pemprosesan, pencirian dan aplikasi yang sesuai dijadikan sebagai bahan rujukan dan panduan kepada pelajar, penyelidik dan pengamal industri.

View
No Thumbnail Available
Publication

Fly ash porous material using geopolymerization process for high temperature exposure

2012 , Mohd. Mustafa Al Bakri Abdullah , Liyana Jamaludin , Kamarudin Hussin , Mohamed Bnhussain , Che Mohd Ruzaidi Ghazali , Mohd Izzat Ahmad

This paper presents the results of a study on the effect of temperature on geopolymers manufactured using pozzolanic materials (fly ash). In this paper, we report on our investigation of the performance of porous geopolymers made with fly ash after exposure to temperatures from 600 °C up to 1000 °C. The research methodology consisted of pozzolanic materials (fly ash) synthesized with a mixture of sodium hydroxide and sodium silicate solution as an alkaline activator. Foaming agent solution was added to geopolymer paste. The geopolymer paste samples were cured at 60 °C for one day and the geopolymers samples were sintered from 600 °C to 1000 °C to evaluate strength loss due to thermal damage. We also studied their phase formation and microstructure. The heated geopolymers samples were tested by compressive strength after three days. The results showed that the porous geopolymers exhibited strength increases after temperature exposure.

View
No Thumbnail Available
Publication

Mechanical Performance, Microstructure, and Porosity Evolution of Fly Ash Geopolymer after Ten Years of Curing Age

2023-02-01 , Aziz I.H.A. , Mohd. Mustafa Al Bakri Abdullah , Rafiza Abd Razak , Zarina Yahya , Mohd Arif Anuar Mohd Salleh , Chaiprapa J. , Rojviriya C. , Vizureanu P. , Sandu A.V. , Muhammad Faheem Mohd. Tahir , Alida Abdullah , Liyana Jamaludin

This paper elucidates the mechanical performance, microstructure, and porosity evolution of fly ash geopolymer after 10 years of curing age. Given their wide range of applications, understanding the microstructure of geopolymers is critical for their long-term use. The outcome of fly ash geopolymer on mechanical performance and microstructural characteristics was compared between 28 days of curing (FA28D) and after 10 years of curing age (FA10Y) at similar mixing designs. The results of this work reveal that the FA10Y has a beneficial effect on strength development and denser microstructure compared to FA28D. The total porosity of FA10Y was also lower than FA28D due to the anorthite formation resulting in the compacted matrix. After 10 years of curing age, the 3D pore distribution showed a considerable decrease in the range of 5–30 µm with the formation of isolated and intergranular holes.