    Preparation of fly Ash-Ladle furnace slag blended geopolymer foam via Pre-Foaming method with polyoxyethylene alkyether sulphate incorporation
    ( 2022)
    Ng Hui-Teng
    ;
    Heah Cheng Yong
    ;
    Liew Yun Ming
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Catleya Rojviriya
    ;
    Hasniyati Md Razi
    ;
    Sebastian Garus
    ;
    Marcin Nabiałek
    ;
    Wojciech Sochacki
    ;
    Ilham Mukriz Zainal Abidin
    ;
    Ng Yong-Sing
    ;
    Andrei Victor Sandu
    ;
    Agata Śliwa
    This paper uses polyoxyethylene alkyether sulphate (PAS) to form foam via pre-foaming method, which is then incorporated into geopolymer based on fly ash and ladle furnace slag. In the literature, only PAS-geopolymer foams made with single precursor were studied. Therefore, the performance of fly ash-slag blended geopolymer with and without PAS foam was investigated at 29–1000 °C. Unfoamed geopolymer (G-0) was prepared by a combination of sodium alkali, fly ash and slag. The PAS foam-to-paste ratio was set at 1.0 and 2.0 to prepare geopolymer foam (G-1 and G-2). Foamed geopolymer showed decreased compressive strength (25.1–32.0 MPa for G-1 and 21.5–36.2 MPa for G-2) compared to G-0 (36.9–43.1 MPa) at 29–1000 °C. Nevertheless, when compared to unheated samples, heated G-0 lost compressive strength by 8.7% up to 1000 °C, while the foamed geopolymer gained compressive strength by 68.5% up to 1000 °C. The thermal stability of foamed geopolymer was greatly improved due to the increased porosity, lower thermal conductivity, and incompact microstructure, which helped to reduce pressure during moisture evaporation and resulted in lessened deterioration.