Effect of temperature and amount of Ag on TiO₂ thin film synthesised via sol–gel method
The effect of polyethylene glycol addition on wettability and optical properties of GO/TiO2 thin film
1 - 2 of 2
No Thumbnail Available
Publication
TiO₂ sol was produced via the sol–gel method with different amounts of AgNO₃ as the source of Ag. The Ag/TiO₂ thin film was obtained by spin coating and was annealed at various annealing temperatures (300°C, 400°C and 500°C) for 1 h. The effect of different amounts of AgNO₃ and different annealing temperatures on the TiO₂ thin films was studied by characterising the phase composition, surface morphology and water contact angle. Results from the x-ray diffraction (XRD) pattern show that with the addition of AgNO₃, Ag/TiO₂ can be formed at low annealing temperatures (300°C). At increased annealing temperatures (400°C and 500°C) and amounts of AgNO₃ (1.0 ml and 1.5 ml), Ag₂O and Ag₃O4 phases were observed. Flakes or flaky islands were formed on the thin film due to thermal expansion mismatch between the film and substrate, residual stress within the film or the release of volatile species when annealed at a low temperature of ⁓300°C. Increasing the temperature to 500°C resulted in the growth and coalescence of the flaky islands by the surface diffusion of adsorbed atoms (adatoms) and their annexation to the surface of existing nuclei. The water contact angle provides valuable insight into the surface interactions between water droplets and the surface of Ag/TiO₂ thin films. It was found that at 1.5 ml AgNO₃, the increased annealing temperature from 300°C to 500°C decreased the water contact angle of Ag/TiO₂ thin films from 83.86° to 34.62°, forming superhydrophilic properties, which indicated its excellent potential as a photocatalyst.
Publication
Modification has been made to TiO2 thin film to improve the wettability and the absorption of light. The sol-gel spin coating method was successfully used to synthesize GO/TiO2 thin films using a titanium (IV) isopropoxide (TTIP) as a precursor. Different amounts of polyethylene glycol (PEG) (20 to 100 mg) were added into the parent sol solution to improve the optical properties and wettability of the GO/TiO2 thin film. The effect of different amounts of PEG was characterized using X-ray diffraction (XRD) for the phase composition, scanning electron microscopy (SEM) for microstructure observation, atomic force microscopy (AFM) for the surface topography, ultraviolet–visible spectrophotometry (UV-VIS) for the optical properties and wettability of the thin films by measuring the water contact angle. The XRD analysis showed the amorphous phase. The SEM and AFM images revealed that the particles were less agglomerated and surface roughness increases from 1.21 × 102 to 2.63 × 102 nm when the amount of PEG increased. The wettability analysis results show that the water contact angle of the thin film decreased to 27.52° with the increase of PEG to 80 mg which indicated that the thin film has hydrophilic properties. The optical properties also improved significantly, where the light absorbance wavelength became wider and the band gap was reduced from 3.31 to 2.82 eV with the presence of PEG.