    Cold-pressed fly ash geopolymers: effect of formulation on mechanical and morphological characteristics
    ( 2021)
    Ong Shee-Ween
    ;
    Heah Cheng Yong
    ;
    Lynette Wei Ling Chan
    ;
    Mohd. Mustafa Al Bakri Abdullah
    ;
    Ho Li Ngee
    ;
    Liew Yun Ming
    ;
    Ooi Wan-En
    ;
    Ng Yong-Sing
    ;
    Nur Ain Jaya
    This research uses low alkali activator content and cold pressing technique for fly ash-based geopolymers formation under room temperature condition. The geopolymers were prepared using four different parameters: fly ash/alkali activator ratio, sodium hydroxide concentration, sodium silicate/sodium hydroxide ratio and pressing force. The results indicated that the compressive strength (114.2 MPa) and flexural strength (29.9 MPa) of geopolymers maximised at a fly ash/alkali activator ratio of 5.5, a 14 M sodium hydroxide concentration, a sodium silicate/sodium hydroxide ratio of 1.5 and a pressing force of 5 tons (pressing stress of 100.0 MPa and 155.7 MPa for compressive and flexural samples, respectively). The degree of reaction (40.1%) enhanced the structure compactness with minimum porosity. The improved mechanical properties confirmed that a high strength pressed geopolymer could be formed at low alkali activator content without the aid of temperature.